Material

Made from high-performance carbon fiber tows pre-impregnated with epoxy resin, with fibers aligned in a single direction.

Thickness Range

From 0.15 mm to 0.6 mm, customizable based on fabric weight and resin content.

Density

1.45 - 1.6 g/cm³, offering lightweight and high-strength characteristics.

Surface Finish

Even resin coating for optimized lamination and molding.

Tensile Strength：≥ 900 MPa

Flexural Strength：≥ 1000 MPa

Temperature Resistance：-40℃ to 180℃

Standard Sizes
Available in rolls with standard widths: 300 mm, 500 mm, or 1000 mm.

Edge Treatment
Heat-cut edges to prevent fiber fraying.

Hardness

High hardness after curing; depends on resin system and curing conditions.

Water Absorption Rate
≤ 0.05%, suitable for humid or changing environments.

Aerospace Industry

Suitable for structural components in aircraft and spacecraft, reducing weight and increasing strength.

Automotive Manufacturing

Used in high-performance racing cars and automotive parts to enhance safety and performance.

Sports Equipment

Applied in high-quality sporting goods, such as bicycle frames and snowboards.

Industrial Equipment

Suitable for high-strength industrial components, increasing durability.